Yesterday I took out the aluminum flat nocks in 4 of my Executioners to replace them with Luminoks. To remove the old nocks, I screwed in a target point, heated it with a torch for 25 - 30 seconds, and then pulled the point/nock out with pliers. Inspecting the arrows where I had just removed the nocks, I noticed a hairline crack running for about 1/2 inch down the shaft of 3 of the 4! Well that’s not good. I know the Luminoks can be a little tight and you might need to shave a tiny bit off to get a good fit but this was before I put them in.
Did I do something wrong here? What could have caused this? These nocks had not been removed before and were the ones in the arrows I bought from Wyvern several months ago. They arrows in question had been shot a good bit - a few hundred times maybe - but I wouldn’t expect this. I didn’t inspect the arrows before removing the nocks so I don’t know if the cracks were already there but I kinda doubt it.
Any help is appreciated.
Cracked Executioners?
Moderator: Excalibur Marketing Dude
- Tangle Eye
- Posts: 133
- Joined: Mon Feb 19, 2018 12:21 am
- Location: Jackson, TN
Cracked Executioners?
———————————————————————————————————
Excalibur Assassin w/ Boo Force 10 string
If you always do what you always did, you’ll always get what you always got.
Excalibur Assassin w/ Boo Force 10 string
If you always do what you always did, you’ll always get what you always got.
Re: Cracked Executioners?
You may have damaged your arrow when you heated them up . You want the lighted nock to fit snug but not to tight that it cracks your arrow. some time you will have to shave one of the knobs off of the nock , just take a little at a time.. if you heat up the field point take a wet paper towel and wrap it around the arrow tip this will help.
W.M.
W.M.
-
- Posts: 1050
- Joined: Thu Jan 25, 2007 4:13 pm
- Location: Western Massachusetts
Re: Cracked Executioners?
Using hot water on the stove will give you a lot more control over the temperature.
Bob
Bob
Vegetarian: vejiˈte(ə)rēən/noun: old Indian word for lousy hunter.
Excalibur Exocet, GT Laser II, 2" Bhoning Blazers 125g NAP Spitfire
Excalibur Exocet, GT Laser II, 2" Bhoning Blazers 125g NAP Spitfire
Re: Cracked Executioners?
Go on You Tube ( How to remove a flat nock cheap, fast, easy ) looks like it will work for you if this helps Yukon
-
- Posts: 2430
- Joined: Sun Dec 18, 2011 6:23 pm
- Location: North Carolina
Re: Cracked Executioners?
By heating them sometimes they will crack, I don't use glue anymore on my aluminum nocks, I order them with the nocks loose. The reasoning behind this is because s I don't glue the nocks I use a plastic sandwich baggie and push the aluminum nock over the baggie and into the back of the arrow. The nock doesn't come out and you can remove them for luminocks anytime you want. Hope this helps.
Stryker Katana 360
Black Eagle Zombie Slayers
TruGlo Titanium X Hybrid Broadheads
Black Eagle Zombie Slayers
TruGlo Titanium X Hybrid Broadheads
- Tangle Eye
- Posts: 133
- Joined: Mon Feb 19, 2018 12:21 am
- Location: Jackson, TN
Re: Cracked Executioners?
Good ideas about the wet paper towel, hot water, and the sandwich bag. I knew I’d get some good ideas here!
———————————————————————————————————
Excalibur Assassin w/ Boo Force 10 string
If you always do what you always did, you’ll always get what you always got.
Excalibur Assassin w/ Boo Force 10 string
If you always do what you always did, you’ll always get what you always got.
Re: Cracked Executioners?
All my BEEs came with press fit nocks installed. No glue on them so no heat is necessary. Just screw in a point and pull them out. You will probably need to cut off a tad of the shaft and refletch before using them again.
Wildlife Population Control Specialist
Re: Cracked Executioners?
Anytime an insert is heated, you run a risk of damaging a shaft. I never try to remove inserts that have been glued in by Cyanoacrylate glues. Methods of removal are not controlled enough for my liking. The pleasure just doesn't outweigh the possible pain.
If someone could figure out the actual amount of heat you can safely apply to a carbon shaft and what amount of heat it takes to compromise the bond of Cyanoacrylate glues, I might change my mind but in the mean time, I'll stick with the known and avoid the unknown.
If someone could figure out the actual amount of heat you can safely apply to a carbon shaft and what amount of heat it takes to compromise the bond of Cyanoacrylate glues, I might change my mind but in the mean time, I'll stick with the known and avoid the unknown.